Reducing the ordering temperature of CoPt nanoparticles by B additive

摘要

We reported the effect of boron addition on magnetic properties and structure of CoPt nanoparticles prepared by a polyol method. The magnetic property measurement showed that the CoPt-B sample exhibited a much larger coercivity compared to the sample without B additive at the same annealing temperature. Transmission electron microscopy and energy dispersive X-ray spectroscopy revealed that the average particle size was about 2 nm for the as-synthesized sample with the ratio of Co and Pt close to 1:1. After annealing, the particle sizes increased but the composition was maintained. The phase transformation of the nanoparticles versus temperature was investigated using a combination of X-ray diffraction and in-situ X-ray absorption analysis. It was shown that the phase transition temperature at which the nanoparticles change from the disordered A1 phase to the ordered L10 phase occurs at temperature of 600 °C. We concluded that boron additives could reduce the ordering temperature of CoPt of about 100 °C.